Vilasari, Elkani (2015) Pengaruh Temperatur Dan Ph Terhadap Kinerja Elektroda Selektif Ion Tiosianat Tipe Kawat Terlapis Berbasis Kitosan-Aliquat 336. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini bertujuan untuk mempelajari pengaruh temperatur dan pH terhadap kinerja elektroda selektif ion (ESI) tiosianat tipe kawat terlapis berbasis kitosan-aliquat 336. ESI tiosianat yang digunakan dalam penelitian ini menggunakan komposisi membran optimum yang terdiri dari kitosan, aliquat 336-tiosianat, dioktilftalat (DOP), dan polivinil klorida (PVC) dengan perbandingan 3% : 0.5% : 60% : 36.5% (b/b) yang dilarutkan dalam tetrahidrofuran (THF) pada perbandingan 1 : 3 (b/v) dengan waktu perendaman optimum dalam larutan NH4SCN 0,1 M selama 25 menit. Pengukuran beda potensial dilakukan pada rentang konsentrasi linier larutan baku kerja tiosianat, yaitu 10-5–10-1 M. Penelitian pengaruh temperatur dilakukan pada rentang temperatur 25-50°C dengan interval kenaikan temperatur 5°C. Sedangkan pengaruh pH dilakukan dengan memvariasi pH larutan baku kerja tiosianat menjadi pH 3-9 dengan interval 1 tingkat pH menggunakan H3PO4 0,01 M dan NaOH 0,01 M. Hasil penelitian menunjukkan bahwa kinerja ESI tiosianat yang dibuat tidak dipengaruhi oleh temperatur 25-35°C (optimum pada 25oC) dan pH 7 (optimum).
English Abstract
The aim of this research is to study the effect of temperature and pH on the performance of thiocyanate ion coated wire electrode (thiocyanate ion CWE) base on chitosan-aliquat 336. Thiocyanate ion CWE used in this study using optimum membrane composition consisting of chitosan, aliquat 336-thiocyanate, dioctyl phthalate (DOP), and polyvinyl chloride (PVC) with ratio 3% : 0.5% : 60% : 36.5% (w/w) which were dissolved in tetrahydrofuran (THF) solvent in ratio 1 : 3 (w/v) with an optimum soaking time in NH4SCN 0.1 M was 25 minutes. Potential measurement made on 10-5-10-1 M of thiocyanate solution as linear concentration range. The effect of temperature on the performance thiocyanate ion CWE was studied at 25-50°C with intervals of 5°C. While the effect of pH was studied by adjusting pH of thiocyanate solution to pH 3-9 with intervals of 1 pH levels using 0.01 M H3PO4 and 0.01 M NaOH. The results showed that the performance of thiocyanate ion CWE was not influenced by temperature of 25-35oC (optimum at 25oC) and pH of 7 (optimum).
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FK/2015/682/ 051506293 |
| Subjects: | 600 Technology (Applied sciences) > 615 Pharmacology and therapeutics > 615.1 Drugs (materia medica) |
| Divisions: | Fakultas Kedokteran > Farmasi |
| Depositing User: | Kustati |
| Date Deposited: | 17 Mar 2016 14:37 |
| Last Modified: | 17 Mar 2016 14:37 |
| URI: | http://repository.ub.ac.id/id/eprint/125478 |
Actions (login required)
 |
View Item |