Oktafiansyah, Rahmad (2017) Studi Pengaruh Waktu Deposisi Lapisan Copper Phthalocyanine (Cupc) Di Atas Quart Crystal Microbalance (Qcm) Terhadap Efektivitas Qcm Sebagai Sensor Kelembaban: Tinjauan Perubahan Frekuensi Qcm Sebagai Respon Perubahan Relative Humidity (Rh). Sarjana thesis, Universitas Brawijaya.
Abstract
Performa Quartz Crystal Microbalance (QCM) sebagai sensor kelembaban dapat ditingkatkan dengan mendeposisikan lapisan matriks pada permukaan QCM. Lapisan matriks meningkatkan adsorpsi molekul uap air pada permukaan QCM, sehingga perubahan frekuensi QCM semakin besar yang menandakan sensor berbasis QCM lebih sensitif. Pada penelitian ini Copper Phthalocyanine (CuPc) dideposisikan diatas QCM menggunakan metode vakum evaporasi dengan variasi waktu deposisi. Morfologi lapisan CuPc dianalisa menggunakan Mikroskop Optik dan TMS-1200 Polytech, sedangkan sudut kontak diukur menggunakan Contact Angle Measurement. Hasil karakterisasi menunjukkan waktu deposisi CuPc yang lebih lama menyebabkan lapisan CuPc yang terbentuk lebih tebal, kasar dan bersifat hidrofobik. Efektivitas QCM dalam deteksi kelembaban diuji dengan mengamati perubahan frekuensi QCM sebagai pengaruh perubahan nilai Relative Humidity (RH). Hasil pengujian menunjukkan lapisan CuPc dengan ketebalan lebih tinggi memiliki respon kelembaban yang lebih baik. Ketebalan dengan respon kelembaban paling baik ditunjukkan oleh waktu deposisi selama 5 menit dengan ketebalan 0,0496 μm, yang memiliki perubahan frekuensi sebesar 1Hz – 3,5Hz. Lapisan yang tebal memiliki respon lebih baik dimungkinkan karena massa CuPc pada permukaan QCM yang lebih banyak menyebabkan interaksi adsorpsi antara CuPc dengan molekul air lebih banyak.
English Abstract
The performance of QCM as humidity sensor can be increased by deposition matrix layer on QCM surface. Matrix layer can increase adsorption of water vapor molecules on QCM surface, so the frequency shift of QCM is larger, so that can indicate the sensor based QCM are more sensitive. In this research Copper Phthalocyanine (CuPc) deposited on QCM by vacuum evaporation method with time various of deposition. The morphology of CuPc film was observed by Microscope Optic and TMS-1200 Polytech, while contact angle of CuPc film was observed by Contact Angle Measurement. The resulth show the morphology of CuPc with more duration cause the formed CuPc film thicker, rougher, and hydrophobyc. Effectiveness of QCM to humidity detection was observed by measuring frequency shift to the Relative Humidity shift. Resulth of testing show, the CuPc layer with higher thickness has better response of humidity change. The thickness layer with best humidity response shown by the time of deposition for 5 minutes with 0,0496μm thickness, which have a change of frequency of 1Hz-3,5Hz. The thicker layer has the better response humidity is possible because the mass of CuPc on QCM surface more causing interaction with more water molecules.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FMIPA/2017/375/051709715 |
| Uncontrolled Keywords: | QCM, CuPc, waktu deposisi, sensor kelembaban, adsorpsi, ketebalan, Relative Humidity |
| Subjects: | 500 Natural sciences and mathematics > 530 Physics |
| Divisions: | Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika |
| Depositing User: | Nur Cholis |
| Date Deposited: | 30 Oct 2017 06:13 |
| Last Modified: | 22 Nov 2021 06:34 |
| URI: | http://repository.ub.ac.id/id/eprint/4555 |
Preview |
Text
BAGIAN DEPAN.pdf Download (190kB) | Preview |
Preview |
Text
DAFTAR PUSTAKA.pdf Download (15kB) | Preview |
Preview |
Text
LAMPIRAN.pdf Download (1MB) | Preview |
Preview |
Text
BAB I.pdf Download (19kB) | Preview |
Preview |
Text
BAB IV.pdf Download (852kB) | Preview |
Preview |
Text
BAB V.pdf Download (8kB) | Preview |
Preview |
Text
BAB II.pdf Download (516kB) | Preview |
Preview |
Text
BAB III.pdf Download (295kB) | Preview |
Actions (login required)
 |
View Item |