Kusumadewi, Intan Rosma and Grenaldi, Angeli Gladis and Prof. Ir. Ludfi Djakfar, MSCE., Ph.D., IPU., ASEAN Eng. and Rahayu Kusumaningrum, ST., MT., M.Sc. (2025) Pengaruh Penambahan Limbah Carrageenan terhadap Kinerja Marshall Campuran Lapis Aus Asbuton (AC-WC Asb). Sarjana thesis, Universitas Brawijaya.
Abstract
Indonesia masih bergantung pada impor aspal meskipun memiliki potensi besar berupa Aspal Buton (Asbuton) yang unggul dengan kandungan aspal alami tinggi dan ketahanan terhadap suhu ekstrem serta beban berat. Namun, Asbuton sering mengalami keretakan akibat nilai flow tinggi pada uji marshall, yang menunjukkan deformasi plastis berlebih dan menurunkan stabilitas perkerasan. Penelitian ini mengevaluasi penambahan limbah carrageenan sebesar 7,25% yang kaya serat selulosa, hemiselulosa, dan lignin, untuk memperkuat ikatan campuran, mengurangi deformasi, menurunkan nilai flow, serta meningkatkan performa dan keberlanjutan campuran aspal, sekaligus mengurangi ketergantungan pada aspal impor. Penelitian ini dilakukan dengan membuat benda uji dari campuran 1.200 gram agregat yang dipanaskan dan dicampur dengan variasi kadar Asbuton B 50/30 (8%, 12%, 16%, 20%) pada suhu 160-170°C. Limbah carrageenan kering yang lolos saringan nomor 200 ditambahkan, kemudian dicampur dengan aspal penetrasi 60/70. Campuran tersebut dipadatkan dalam cetakan dan didiamkan selama 24 jam sebelum diuji karakteristik marshall. Kesimpulan penelitian ini menunjukkan bahwa peningkatan kadar Asbuton dalam campuran lapis aus aspal berpengaruh pada penurunan beberapa parameter marshall seperti VMA, VIM, stabilitas, dan Marshall Quotient (MQ), dengan kadar Asbuton tanpa limbah carrageenan sekitar 13,2%. Penambahan limbah carrageenan memungkinkan kadar Asbuton naik hingga 14% dengan karakteristik yang masih memenuhi standar. Nilai optimum Asbuton adalah 10,6% tanpa aditif dan 11,0% dengan limbah carrageenan. Diperlukan metode pengeringan limbah carrageenan yang lebih baik dan peningkatan kadar penambahan untuk meningkatkan karakteristik marshall.
English Abstract
Indonesia is still dependent on imports of asphalt despite having great potential in the form of Buton Asphalt (Asbuton) which excels with high natural asphalt content and resistance to extreme temperatures and heavy loads. However, Asbuton often cracks due to high flow values in marshall tests, which indicates excessive plastic deformation and decreases pavement stability. This study evaluates the addition of 7.25% waste carrageenan, which is rich in cellulose, hemicellulose, and lignin fibers, to strengthen the mixture bond, reduce deformation, decrease flow values, and improve the performance and sustainability of asphalt mixtures, while reducing dependence on imported asphalt. This research was conducted by making test specimens from a mixture of 1,200 grams of aggregates heated and mixed with various levels of Asbuton B50/30 (8%, 12%, 16%, 20%) at a temperature of 160-170°C. Dried carrageenan waste passing sieve number 200 was added, then mixed with 60/70 penetration asphalt. The mixture was compacted in a mold and allowed to stand for 24 hours before being tested for marshall characteristics. The conclusion of this research shows that increasing the level of Asbuton in asphalt wear layer mixtures affects the decrease of several Marshall parameters such as VMA, VIM, stability, and Marshall Quotient (MQ), with Asbuton levels without carrageenan waste around 13.2%. The addition of carrageenan waste allows the Asbuton content to increase to 14% with characteristics that still meet the standards. The optimum value of Asbuton is 10.6% without additives and 11.0% with carrageenan waste. A better method of drying the carrageenan waste and increasing the addition level is required to improve the marshall characteristics.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 052507 |
| Uncontrolled Keywords: | AC-WC Asb, Asbuton, Limbah Carrageenan, Marshall, VMA, VIM, VFB, Stabilitas, Flow, MQ |
| Divisions: | Fakultas Teknik > Teknik Sipil |
| Depositing User: | S Sucipto |
| Date Deposited: | 13 Jun 2025 03:39 |
| Last Modified: | 13 Jun 2025 03:39 |
| URI: | http://repository.ub.ac.id/id/eprint/241216 |
![[thumbnail of DALAM MASA EMBARGO]](https://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (DALAM MASA EMBARGO)
-Angeli Gladis Grenaldi.pdf Restricted to Registered users only Download (7MB) |
Actions (login required)
 |
View Item |