Pengaruh Penggunaan Agregat Kasar Expanded Polystyrene Berukuran Satu Sentimeter dengan Coating Pasta Semen terhadap Kuat Tekan dan Modulus Elastisitas Beton dengan Metode Non-Destructive Test

Putra, Vito Tristanio and Ir. Indra Waluyohadi, S.T., M.T., M.Sc., IPM and Dr. Eng. Devi Nuralinah, ST., MT. (2025) Pengaruh Penggunaan Agregat Kasar Expanded Polystyrene Berukuran Satu Sentimeter dengan Coating Pasta Semen terhadap Kuat Tekan dan Modulus Elastisitas Beton dengan Metode Non-Destructive Test. Sarjana thesis, Universitas Brawijaya.

Abstract

Infrastruktur sangat penting untuk mendorong kemajuan sosial, ekonomi, dan pemerataan pembangunan nasional. Kebutuhan akan bahan konstruksi, terutama beton, meningkat sebagai akibat dari pertumbuhan infrastruktur yang pesat. Beton adalah komposit yang terdiri dari semen, agregat (batu kecil atau pasir), dan air. Namun, penggunaan yang berlebihan menyebabkan kehilangan sumber daya alam dan energi. Dalam dua puluh tahun terakhir, konsumsi agregat alam total mencapai 48,3 miliar ton. Untuk itu, penggunaan bahan alternatif yang ramah lingkungan seperti styrofoam atau limbah expanded polystyrene (EPS) sebagai pengganti agregat kasar diperlukan. Limbah polystyrene yang diperluas adalah limbah yang sulit terurai secara alami. 270.000–590.000 ton limbah expanded polystyrene mencemari laut Indonesia setiap tahun. Dalam beton ringan, penggunaan expanded polystyrene dapat menggantikan agregat alam dan mengurangi limbah lingkungan. Beton ringan berbahan expanded polystyrene memiliki keunggulan dalam mengurangi berat, tetapi kekuatannya cenderung lebih rendah dibanding beton normal. Penggunaan expanded polystyrene yang berlebihan juga dapat menyebabkan beton menjadi kurang kuat. Salah satu cara untuk meningkatkan kekuatan expanded polystyrene adalah dengan melapisinya dengan pasta semen. Pasta semen berfungsi sebagai pelindung dan meningkatkan daya ikat material. Tujuan penelitian ini adalah untuk mempelajari penggunaan expanded polystyrene sebagai pengganti agregat kasar dan bagaimana penggunaan expanded polystyrene mempengaruhi kekuatan tekan beton dan modulus elastisitas. Lima jenis beton yang berbeda digunakan dalam penelitian ini: 25% EPS, 50% EPS, 75% EPS, 100% EPS, dan NCA sebagai kontrol. Hasil pengujian menunjukkan bahwa agregat kasar expanded polystyrene dengan penutup pasta semen menurunkan modulus elastisitas dan nilai tekan, dibandingkan dengan beton yang dibuat dengan agregat kasar alami. Uji hammer, UPV, kompresi, dan analisis SonReb digunakan sebagai metode pengujian.

English Abstract

Infrastructure is very important to drive social, economic, and equitable national development. The demand for construction materials, especially concrete, has increased as a result of rapid infrastructure growth. Concrete is a composite consisting of cement, aggregates (small stones or sand), and water. However, excessive use leads to the depletion of natural resources and energy. In the past twenty years, the total consumption of natural aggregates has reached 48.3 billion tons. For this reason, the use of environmentally friendly alternative materials such as styrofoam or expanded polystyrene (EPS) waste as a substitute for coarse aggregate is necessary. Expanded polystyrene waste is waste that is difficult to decompose naturally. 270,000– 590,000 tons of expanded polystyrene waste pollute the seas of Indonesia every year. In lightweight concrete, the use of expanded polystyrene can replace natural aggregates and reduce environmental waste. Lightweight concrete made with expanded polystyrene has the advantage of reducing weight, but its strength tends to be lower compared to normal concrete. Excessive use of expanded polystyrene can also cause the concrete to become weaker. One way to increase the strength of expanded polystyrene is by coating it with cement paste. The cement paste serves as a protective layer and enhances the material's bonding strength. The purpose of this research is to study the use of expanded polystyrene as a substitute for coarse aggregate and how the use of expanded polystyrene affects the compressive strength of concrete and the modulus of elasticity. Five different types of concrete were used in this study: 25% EPS, 50% EPS, 75% EPS, 100% EPS, with NCA as the control. The test results show that expanded polystyrene coarse aggregate with a cement paste coating reduces the modulus of elasticity and compressive strength compared to concrete made with natural coarse aggregate. Hammer test, UPV, compression, and SonReb analysis were used as testing methods.

Item Type:	Thesis (Sarjana)
Identification Number:	0525070025
Uncontrolled Keywords:	Expanded polystyrene, Non-destructive test, Beton ringan-Expanded polystyrene, Non-destructive test, Lightweight concrete
Divisions:	Fakultas Teknik > Teknik Sipil
Depositing User:	Sugeng Moelyono
Date Deposited:	24 Feb 2025 08:18
Last Modified:	24 Feb 2025 08:18
URI:	http://repository.ub.ac.id/id/eprint/237025

Text (DALAM MASA EMBARGO) Vito Tristanio Putra.pdf Restricted to Registered users only Download (10MB)

Actions (login required)

View Item