Optimasi Kekuatan Tarik Sambungan Las Gesek Poros AA6061 Dengan Variasi Sudut Chamfer Ganda Tinggi 2 mm, Waktu Gesek dan Gaya Tekan Akhir Menggunakan Response Surface Methodology

Wiratama, Adhika and Dr. Eng. Yudy Surya Irawan, ST., M.Eng. and Moch. Syamsul Ma’arif, ST., MT. (2024) Optimasi Kekuatan Tarik Sambungan Las Gesek Poros AA6061 Dengan Variasi Sudut Chamfer Ganda Tinggi 2 mm, Waktu Gesek dan Gaya Tekan Akhir Menggunakan Response Surface Methodology. Sarjana thesis, Universitas Brawijaya.

Abstract

Pada era modern seperti sekarang ini perkembangan teknologi sangat penting dalam dunia industri dan manufaktur. Salah satu material yang digunakan adalah aluminium A6061. Aluminium A6061 memiliki kekuatan mekanik yang cukup tinggi, tahan terhadap korosi, mudah dalam pembentukan dan sifat mampu las yang baik. Material ini tergolong sulit untuk dilakukan proses pengelasan cair. Metode yang paling efektif untuk merealisasikan hal tersebut yaitu dengan metode pengelasan gesek (friction welding). Dalam penelitian ini bertujuan untuk mengoptimalkan pengaruh sudut chamfer,waktu gesek dan gaya tekan akhir terhadap kekuatan tarik sambungan las dengan material simillar aluminium A6061 dalam proses rotary friction welding. Metode penelitian yang digunakan yaitu eksperimen yang nyata (true experimental). Dengan variasi percobaan berdasarkan rancangan percobaan RSM pemodelan box-behnken design untuk mendapat kombinasi variabel hasil optimasi. Sehingga dapat diketahui hasil optimal kekuatan tarik sambungan las gesek poros AA6061 dengan variasi sudut chamfer ganda tinggi 2 mm, waktu gesek dan gaya tekan akhir menggunakan metode response surface methodology. Pada penelitian ini digunakan variasi sudut chamfer 20,45 dan 70 ,kemudian waktu gesek 5,7,9 detik dan gaya tekan akhir 4,9 kN,16,45 kN dan 28 kN. Hasil penelitian ini didapat nilai keuatan tarik tertinggi pada spesimen kekuatan optimasi dengan sudut chamfer 20,waktu gesek 5 detik dan gaya tekan akhir 28 kN sebesar 160,76 MPa. Lalu spesimen kekuatan tarik tertinggi dengan sudut chamfer 20,waktu gesek 7 detik dan gaya tekan akhir 28 kN sebesar 147,26 MPa. Kemudian spesimen kekuatan tarik terendah dengan sudut chamfer 70,waktu gesek 7 detik dan gaya tekan akhir 4,9 kN sebesar 57,27 Mpa dan spesimen pembanding dengan sudut chamfer 90,waktu gesek 5 detik dan gaya tekan akhir 28 kN sebesar 117,39 MPa.

English Abstract

In this modern era, technological development is very important in the world of industry and manufacturing. One of the materials used is aluminium A6061. Aluminum A6061 has high mechanical strength, corrosion resistance, easy forming and good weldability. This material is relatively difficult to do the liquid welding process. The most effective method to realize this is the friction welding method. This study aims to optimize the effect of chamfer angle, friction time,and upset pressure on the tensile strength of welded joints with A6061 aluminium simillar material in the rotary friction welding process. The research method used is true experimental. With experimental variations based on the experimental design RSM modeling box-behnken design to get a combination of variables optimization results. So that it can be known the optimal results of the tensile strength of the AA6061 shaft friction welding connection with a variation of the double chamfer angle of 2 mm high, friction time,and upset force using the response surface methodology. In this study, variations of chamfer angles of 20°, 45° and 70° were used, then friction times of 5, 7, 9 seconds and upset forces of 4.9 kN, 16.45 kN and 28 kN. The results of this study obtained the highest tensile strength value in the optimization strength specimen with a chamfer angle of 20°, friction time of 5 seconds and upset force of 28 kN of 160.76 MPa. Then the highest tensile strength specimen with a chamfer angle of 20°, friction time of 7 seconds and upset force of 28 kN amounted to 147.26 MPa. Then the lowest tensile strength specimen with a chamfer angle of 70°, friction time of 7 seconds and upset force of 4.9 kN of 57.27 MPa and comparison specimen with a chamfer angle of 90°, friction time of 5 seconds and upset force of 28 kN of 117.39 MPa.

Item Type:	Thesis (Sarjana)
Identification Number:	0524070111
Uncontrolled Keywords:	Aluminium A6061, Pengelasan Gesek, Response Surface Methodology, Box- Bhenken Design, Kekuatan Tarik-Aluminium A6061, Friction Welding, Response Surface Methodology, Box- Bhenken Design, Tensile Strength.
Divisions:	Fakultas Teknik > Teknik Mesin
Depositing User:	Sugeng Moelyono
Date Deposited:	15 May 2024 07:29
Last Modified:	15 May 2024 07:29
URI:	http://repository.ub.ac.id/id/eprint/218826

Text (DALAM MASA EMBARGO) Adhika Wiratama.pdf Restricted to Registered users only Download (18MB)

Actions (login required)

View Item