Purbosari, Andhini and Mupangati, Anindha Eka (2019) Pembuatan Granule Karbon Aktif dan Na-Bentonit untuk Pemurnian Minyak Goreng Bekas. Sarjana thesis, Universitas Brawijaya.
Abstract
Proses adsorpsi pada pemurnian minyak goreng bekas telah banyak dilakukan untuk meningkatkan kualitas minyak goreng bekas yang akan digunakan sebagai bahan baku biodiesel. Berdasarkan pada beberapa penelitian yang telah dilakukan, proses adsorpsi dilakukan dengan menggunakan adsorben berbentuk serbuk secara kontinyu dalam kolom. Namun terdapat kendala ketika proses adsorpsi berlangsung, yaitu terjadinya proses flooding. Flooding akan mengurangi efektifitas proses adsorpsi. Oleh karena itu, dilakukan penelitian adsorpsi minyak goreng bekas dengan menggunakan adsorben berbentuk granul. Pada dasarnya, adsorben granul diharapkan mampu mengurangi efek flooding yang terjadi karena adsorben granul memiliki void fraction yang lebih besar jika dibandingkan dengan adsorben serbuk, sehingga fluida akan lebih mudah mengalir dan proses adsorpsi dapat berjalan lebih efektif. Penelitian ini bertujuan untuk mengetahui pengaruh rasio massa karbon aktif dan Na-Bentonit terhadap karakteristik adsorben dan mengetahui kinerja adsorben granul pada aplikasi pemurnian minyak goreng bekas menggunakan kolom adsorpsi. Penelitian ini diawali dengan pembuatan karbon aktif dari serabut kelapa dengan proses karbonisasi pada 600 °C selama 70 menit. Serabut kelapa dipilih sebagai bahan baku karbon aktif karena memiliki kandungan selulosa dan hemiselulosa yang cukup tinggi, yaitu 43% dan 20%. Setelah proses pembuatan karbon aktif, dilanjutkan dengan proses pembuatan adsorben granul dengan proses granulasi menggunakan perekat waterglass. Adsorben granul dibuat dengan variasi rasio massa karbon aktif dan Na-Bentonit, yaitu karbon aktif 100%, karbon aktif 90% dengan Na-Bentonit 10%, dan karbon aktif 80% dengan Na-Bentonit 20%, serta Na-Bentonit. Pada setiap variabel dilakukan karakterisasi terhadap kadar air, kadar abu, kadar bahan menguap pada pemanasan 950 °C, dan daya serap terhadap metilen biru untuk mengetahui pengaruh karbon aktif dan Na-Bentonit. Standar karakterisasi pada adsorben granul mengacu pada SNI 06-3730-1995 tentang arang aktif teknis butiran. Kinerja adsorben dapat diketahui dengan melakukan pengujian terhadap adsorben pada proses adsorpsi minyak goreng bekas secara kontinyu selama 120 menit terhadap penurunan kadar asam lemak bebas dan kadar air minyak goreng bekas. Hasil penelitian yang didapatkan menyatakan bahwa karbon aktif 100%, karbon aktif 90% dengan Na-Bentonit 10%, dan karbon aktif 80% dengan Na-Bentonit 20% memenuhi nilai SNI 06-3730-1995. Karakteristik yang paling baik dimiliki oleh karbon aktif 80% dengan Na-bentonit 20% karena memiliki daya serap terhadap metilen biru sebesar 378,24 mg/g. Jika dilihat dari kinerja adsorben pada proses adsorpsi minyak goreng bekas, karbon aktif 80% dengan Na-Bentonit 20% mempunyai kinerja terbaik,karena dapat mereduksi kadar FFA hingga 94,38% dan air hingga 74,54%.
English Abstract
Adsorption process in purifying waste cooking oil has been applied for increasing the quality of waste cooking oil to be used as raw material for biodiesel. Recent research, show that adsorption process has been done by using powdered adsorbent in continuous process column. Nevertheless, flooding happened during adsorption as a problem. Flooding can decrease the effectivity of adsorption process. Therefore, research about waste cooking oil adsorption is done by using granule adsorbent. Basically, granule adsorbent is expected to decrease the flooding effect because granule has a larger void fraction than powdered. Consequently, fluid will be easily flowing through the adsorbent and the adsorption process become effective. The objectives of this research are discovering the effect of mass ratio of mixing activated carbon and Na-bentonite towards the adsorbent characteristics and discovering the adsorbent performances in purifying waste cooking oil in continuous adsorption column. This research was started with producing activated carbon from coconut fiber through carbonization process in 600 °C for 70 minutes. Coconut fiber was used due to its composition of cellulose and hemicellulose, that is 43% and 20% respectively. After producing activated carbon, it was continued with producing of granule adsorbent through granulation by waterglass as a binder. Granule adsorbents were varied into 4 variables, they were 100% activated carbon, 90% activated carbon with 10% Na-bentonite, 80% activated carbon with 20% Na-bentonite, and Na-bentonite. Each of the variables was charachterized for moisture content, ash content, volatile matter content at 950 °C heating, and methylene blue adsorption capacity to discover the effect of mixture of activated carbon and Na-bentonite. The characterization standard of granule adsorbent refers to SNI 06-3730-1995 for granule technical activated carbon. Performance of adsorbents are known by doing adsorption of waste cooking oil for 120 minutes continuously to reduce the FFA content and moisture content of waste cooking oil. The result of the research showed that 100% activated carbon, 90% activated carbon with 10% Na-bentonite, 80% activated carbon with 20% Na-bentonite, and Na-bentonite are fulfilled the value of SNI 06-3730-1995. The mixture of 80% activated carbon and 20% Na-Bentonit is the best characteristic, because it has the largest methylene blue adsorption capacity, that is 378.24 mg/g. From the aspect of adsorbent performance in waste cooking oil adsorption, 80% activated carbon with 20% Na-bentonite has the best performance, because it has thelargest FFA reduction to 94.38% unit area and water reduction to 74.54%.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FT/2019/622/051905184 |
| Uncontrolled Keywords: | Adsorpsi, Granul, Karbon Aktif, Minyak Goreng Bekas, Na-Bentonit, Activated carbon, Adsorption, Granule, Na-Bentonite, Waste Cooking Oil |
| Subjects: | 600 Technology (Applied sciences) > 662 Explosives of explosives, fuels, related products > 662.9 Nonfuel carbons > 662.93 Adsorbent carbons |
| Divisions: | Fakultas Teknik > Teknik Kimia |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 05 Aug 2020 07:30 |
| Last Modified: | 15 Aug 2020 05:47 |
| URI: | http://repository.ub.ac.id/id/eprint/172876 |
Actions (login required)
 |
View Item |