Pengaruh Fraksi Volume Serat Kulit Waru (Hibiscus Tiliaceus) Terhadap Kekuatan Tarik Komposit Epoxy

Prawestin, Amanda Dea (2017) Pengaruh Fraksi Volume Serat Kulit Waru (Hibiscus Tiliaceus) Terhadap Kekuatan Tarik Komposit Epoxy. Sarjana thesis, Universitas Brawijaya.

Abstract

Kebutuhan pada bahan berbahan komposit semakin tinggi, sudah banyak alat-alat sehari-hari yang diproduksi dari bahan berbahan komposit. Teknologi komposit dengan material serat alam (Natural Fiber) merupakan pemanfaatan serat alam sebagai bahan penguat matrik komposit, pemanfaatan serat alam ini memberikan keuntungan seperti jumlahnya yang berlimpah, memiliki specific cost yang rendah, dapat diperbarui, serta tidak mencemari lingkungan. Waru (Hibiscus tiliaceus) merupakan jenis tanaman yang dikenal oleh penduduk indonesia. Jenis ini banyak ditemukan dengan mudah karena tersebar luas di daerah tropis dan tumbuh berkelompok di pantai berpasir atau daerah pasang surut. Disisi lain Kulit Waru (Hibiscus Tiliaceus) kurang dimanfaatkan secara maksimal oleh masyarakat oleh karena itu akan sangat menguntungkan apabila dapat merubah kulit waru menjadi bahan baku pembuatan komposit. Tujuan penelitian ini adalah untuk mengetahui pengaruh penambahan fraksi volume serat terhadap kekuatan tarik komposit. penelitian ini menggunakan metode kuantitatif eksperimental dengan melakukan variasi fraksi volume serat sebanyak 15%, 25%, 35%, dan 45% yang masing-masing dilakukan pengulangan pengujian sebanyak tiga kali. Hasil yang diperoleh bahwa hasil kekuatan tarik tertinggi terdapat pada fraksi volume serat 45% sebesar 68.82 MPa dengan beban tarik sebesar 1651.97 N dan kuat tarik terendah pada fraksi volume serat 15% sebesar 46.49 MPa dengan beban tarik sebesar 1091.99 N

English Abstract

Need for composite materials is higher, there many daily tools produced from materials made from composites. Technology of composite with natural fiber material is benefits of natural fiber as a composite matrik material, benefits of this natural fiber provides advantages such as abundant amount, has a low specific cost, can be updated, and not pollute the environment. Waru (Hibiscus tiliaceus) is a type of plant famous by the people of Indonesia. Species of waru is many found because it is spread in the tropics and grows in clusters on sandy beaches or tidal areas. The other side Waru (Hibiscus Tiliaceus) Leather is not utilized maximally by society therefore it will be very beneficial if it can change skin waru become raw material of composite manufacture. The purpose of this research was to determine the effect of adding fiber volume fraction to composite tensile strength.This research uses quantitative experimental method by variation of fiber volume fraction as much as 15%, 25%, 35%, and 45% which each repeated testing three repetition.The obtained result that the highest tensile strength was found in the fraction of 45% fiber volume of 68.82 MPa with a tensile load of 1651.97 N and the lowest tensile strength at a fraction of 15% fiber volume of 46.49 MPa with a tensile load of 1091.99 N

Item Type: Thesis (Sarjana)
Identification Number: SKR/FTP/2017/589/051710046
Uncontrolled Keywords: Serat Kulit Waru (Hibiscus Tiliaceus), Fraksi Volume Serat, Komposit.
Subjects: 600 Technology (Applied sciences) > 620 Engineering and allied operations > 620.1 Engineering mechanics and materials > 620.19 Other engineering materials > 620.197 Organic fibrous materials
Divisions: Fakultas Teknologi Pertanian > Keteknikan Pertanian
Depositing User: Yusuf Dwi N.
Date Deposited: 26 Oct 2017 01:18
Last Modified: 23 Oct 2021 11:46
URI: http://repository.ub.ac.id/id/eprint/4406
[thumbnail of 050903037.pdf] Text
050903037.pdf
Restricted to Registered users only

Download (2MB)

Actions (login required)

View Item View Item