Pengaruh Perbedaan Konsentrasi Sds Pada Perendaman 21 Hari Tendon Achilles Ayam Terhadap Sisa Sel Dan Ketebalan Serabut Kolagen Pada Proses Deselularisasi

Meizya, Hikmah Maulindah and drh. Fajar Shodiq Permata, M, Biotech (2024) Pengaruh Perbedaan Konsentrasi Sds Pada Perendaman 21 Hari Tendon Achilles Ayam Terhadap Sisa Sel Dan Ketebalan Serabut Kolagen Pada Proses Deselularisasi. Sarjana thesis, Universitas Brawijaya.

Abstract

Deselularisasi merupakan proses untuk menghilangkan sel tanpa merusak ECM pada jaringan. Proses deselularisasi umumnya menggunakan bahan kimia, salah satunya Sodium Dodecyl Sulphate. Penelitian ini bertujuan untuk mengetahui pengaruh SDS dengan konsentrasi yang berbeda dalam proses deselularisasi. Terdapat 20 sampel yang dibagi menjadi 4 perlakuan yaitu Kontrol (K), SDS 0,1% (SA), SDS 0,5% (SB), dan SDS 1% (SC). Setiap perlakuan terdapat 5 sample yang direndam selama 21 hari, setiap 3 hari, larutan akan diganti. Perhitungan sel menggunakan pewarnaan HE, sementara ketebalan serabut kolagen menggunakan pewarnaan Masson’s Trichrome yang diamati pada mikroskop Cahaya perbesaran 400x. Pengolahan data sel menggunakan uji Kruskal-Wallis, uji Pairwise dengan p value < 0,05, dan uji Spearman Correlation. Untuk data ketebalan serabut kolagen menggunakan uji One Way Anova, uji Tukey dengan p-value < 0,05 dan uji Spearman Correlation dengan p-value < 0,05. Hasil terkait jumlah sel menunjukkan bahwa peningkatan konsentrasi SDS mampu mempengaruhi mempengaruhi jumlah sel yang ditunjukkan pada nilai uji Kruskal-Wallis sebesar p = 0,005 (p-value<0,05) namun tidak memiliki korelasi dengan kenaikan konsentrasi SDS terhadap penurunan jumlah sel (p = 0,545 dan r = -0,170). Hasil terkait ketebalan serabut kolagen menunjukkan bahwa peningkatan konsentrasi SDS mampu mempengaruhi ketebalan serabut kolagen yang ditunjukkan pada nilai uji ANOVA sebesar p = 0,003 (p-value<0,05), namun tidak memiliki korelasi terhadap tingginya konsentrasi SDS menyebabkan ketebalan serabut kolagen menurun (p = 0,443 dan r = -0,214). Berdasarkan jumlah sel dan ketebalan serabut kolagen, disimpulkan bahwa peningkatan konsentrasi larutan SDS mampu mempengaruhi jumlah sel namun tidak mempengaruhi ketebalan serabut kolagen.

English Abstract

Decellularization is a process to remove cells without damaging the ECM in the tissue. The decellularization process generally uses chemicals, one of which is Sodium Dodecyl Sulphate. This study aims to determine the effect of SDS with different concentrations in the decellularization process. There were 20 samples divided into 4 treatments, namely Control (K), SDS 0.1% (SA), SDS 0.5% (SB), and SDS 1% (SC). Each treatment has 5 samples soaked for 21 days, every 3 days, the solution will be replaced. Cell counts used HE staining, while collagen fiber thickness used Masson’s Trichrome staining observed on a 400x magnification Light microscope. Cell data processing used the Kruskal-Wallis test, the Pairwise test with p-value <0.05, and the Spearman Correlation test. For collagen fiber thickness data using the One Way ANOVA test, Tukey test with p-value < 0.05, and Spearman Correlation test with p-value < 0.05. The results related to the number of cells showed that an increase in SDS concentration was able to affect the number of cells as shown in the Kruskal-Wallis test value of p = 0.005 (p-value <0.05) but had no correlation with the increase in SDS concentration to the decrease in cell number (p = 0.545 and r = -0.170). The results related to the thickness of collagen fibers showed that increasing the concentration of SDS was able to affect the thickness of collagen fibers as shown in the ANOVA test value of p = 0.003 (p-value <0.05), but did not correlate with the high concentration of SDS causing the thickness of collagen fibers to decrease (p = 0.443 and r = -0.214). Based on the number of cells and the thickness of collagen fibers, it is concluded that increasing the concentration of SDS solution can affect the number of cells but not the thickness of collagen fibers.

Item Type:	Thesis (Sarjana)
Identification Number:	0524130017
Uncontrolled Keywords:	Deselularisasi, SDS, Tendon Achilles ayam, Scaffold, tissue engineering
Divisions:	Fakultas Kedokteran Hewan > Kedokteran Hewan
Depositing User:	Unnamed user with username nova
Date Deposited:	03 Jun 2024 06:54
Last Modified:	03 Jun 2024 06:54
URI:	http://repository.ub.ac.id/id/eprint/219544

Text (DALAM MASA EMBARGO) Hikmah Maulindah Meizya.pdf Restricted to Registered users only Download (4MB)

Actions (login required)

View Item