Monique, Keziah and Dr. dr. Retty Ratnawati, M.Sc. (2023) Pengaruh Aplikasi Gliserin Pada Kekuatan Tekan Resin Komposit Nanofiller Dengan Perendaman Obat Kumur Beralkohol. Sarjana thesis, Universitas Brawijaya.
Abstract
Resin komposit merupakan jenis bahan tumpatan yang cukup sering digunakan dalam kedokteran gigi karena mempunyai nilai estetis yang tinggi. Resin komposit mempunyai beberapa sifat mekanis salah satunya yaitu kekuatan tekan yang digunakan untuk mengetahui kemampuan dari material tumpatan dalam menahan beban kunyah. Resin komposit dapat menyerap air yang mengakibatkan degradasi apabila terkena cairan dalam rongga mulut seperti obat kumur beralkohol. Polimerisasi resin komposit akan terganggu apabila terkena oksigen di lingkungan sekitar yang menyebabkan berkurangnya kinerja fotoinsiator dan stabilisasi radikal bebas dan terbentuk OIL yang dapat mengurangi kekuatan tekan resin komposit. Penambahan gliserin pada permukaan resin komposit selama proses curing untuk mengurangi OIL. Metode penelitian ini adalah experimental laboratories dengan rancangan penelitian post test only grup design. Uji statistik menggunakan uji One Way ANOVA menunjukkan nilai signifikansi ≤ 0,05 (0,000), sehingga terdapat perbedaan kekuatan tekan pada K1, K2, K3, K4, K5, dan K6. Dari hasil penelitian diketahui bahwa pengaplikasian gliserin dan perendaman obat kumur beralkohol berpengaruh terhadapa kekuatan tekan. Rata-rata nilai kekuatan tekan paling tinggi terjadi pada kelompok 2 yang diaplikasikan gliserin tanpa dilakukan perendaman obat kumur beralkohol. Rata-rata nilai kekuatan tekan yang paling rendah terjadi pada kelompok 6 yang tanpa diaplikasikan gliserin dan dilakukan perendaman obat kumur beralkohol selama 12 jam
English Abstract
Composite resin is a type of filling material that is often used in dentistry because it has a high aesthetic value. Composite resin has several mechanical properties, one of which is compressive strength which is used to determine the ability of the filling material to withstand chewing loads. Composite resins can absorb water which results in degradation when exposed to liquids in the oral cavity such as alcoholic mouthwashes. Composite resin polymerization will be disrupted if it is exposed to oxygen in the surrounding environment which causes a reduction in photoinitiator performance and free radical stabilization and the formation of OIL which can reduce the compressive strength of composite resin. The addition of glycerin on the surface of the composite resin during the curing process to reduce OIL. This research method was an experimental laboratory with a post test only research group design. Statistical tests using the One Way ANOVA test showed a significance value of ≤ 0.05 (0.000), so that there were differences in compressive strength at K1, K2, K3, K4, K5, and K6. From the results it was known that the application of glycerin and immersion of alcoholic mouthwash affect the compressive strength. The highest average value of compressive strength occurred in group 2 which was applied glycerin without immersing alcoholic mouthwash. The lowest average value of compressive strength occurred in group 6 which did not apply glycerin and soaked in alcoholic mouthwash for 12 hours
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | 052314 |
| Uncontrolled Keywords: | Resin komposit nanofiller, kekuatan tekan, gliserin, obat kumur beralkohol - Nanofiller resin composite, compressive strength, glycerin, alcoholic mouthwash. |
| Divisions: | Fakultas Kedokteran Gigi > Kedokteran Gigi |
| Depositing User: | Emy Sukartini |
| Date Deposited: | 10 Jan 2024 07:37 |
| Last Modified: | 10 Jan 2024 07:37 |
| URI: | http://repository.ub.ac.id/id/eprint/207535 |
![[thumbnail of Dalam masa EMBARGO]](http://repository.ub.ac.id/style/images/fileicons/text.png) |
Text (Dalam masa EMBARGO)
Keziah Monique.pdf Restricted to Registered users only until 31 December 2025. Download (2MB) |
Actions (login required)
 |
View Item |