Perbedaan Nilai Kekasaran Permukaan GIC, RMGIC, dan Nananoionomer Setelah Penyikatan dengan Pasta Gigi yang Mengandung Charcoal

Katili, Juliastri Maria and drg. Lalita El Milla,, M.Si (2020) Perbedaan Nilai Kekasaran Permukaan GIC, RMGIC, dan Nananoionomer Setelah Penyikatan dengan Pasta Gigi yang Mengandung Charcoal. Sarjana thesis, Universitas Brawijaya.

Abstract

Latar Belakang: Nanoionomer merupakan perkembangan terbaru dari ionomer cement. Salah satu faktor terpenting yang mempengaruhi ketahanan restorasi di dalam rongga mulut adalah tekstur permukaan restorasi tersebut. Tekstur permukaan restorasi dapat dipengaruhi oleh proses penyikatan dan kandungan bahan abrasif pada pasta gigi. Charcoal merupakan salah satu bahan abrasif yang dapat mempengaruhi tekstur permukaan restorasi. Tujuan: Penelitian ini bertujuan untuk mengetahui perbedaan nilai kekasaran permukaan GIC, RMGIC dan Nanoionomer setelah dilakukan penyikatan dengan pasta gigi yang mengandung charcoal. Metode: Penelitian eksperimental laboratoris dengan desain pre and post test control group design; sebanyak 24 sampel dibagi menjadi 6 kelompok. Sampel pada kelompok kontrol disikat dengan aquadest dan sampel pada kelompok perlakuan disikat dengan pasta gigi yang mengandung charcoal dengan durasi penyikatan selama 60 menit. Pengukuran nilai kekasaran permukaan (Ra) dilakukan menggunakan Surface Roughness Tester Mitutoyo SJ-210. Data hasil penelitian kemudian dianalisa secara statistik. Hasil: Hasil uji statistik menunjukkan terdapat perbedaan bermakna (p<0.05) pada rata-rata nilai kekasaran permukaan GIC, RMGIC dan Nanoionomer setelah dilakukan penyikatan dengan pasta gigi yang mengandung charcoal. Kesimpulan: Terdapat perbedaan nilai kekasaran permukaan GIC, RMGIC dan Nanoionomer setelah penyikatan dengan pasta gigi yang mengandung charcoal.

English Abstract

Background: Nanoionomer is the latest development of ionomer cement. Surface texture of the restoration could affect the resistance of restoration in the oral cavity. The surface texture of the restoration can be identified by brushing and the use of abrasive content in toothpaste. Charcoal is an abrasive material that can affect surface texture of restoration. Purpose: This study aims to determine difference in surface roughness value of GIC, RMGIC and Nanoionomer after brushing with toothpaste containing charcoal. Methods: Laboratory experimental research was conducted with a pre and post test control group design; as many as 24 samples were divided into 6 groups. Samples in the control group were brushed with aquadest and samples in the treatment group were brushed with toothpaste containing charcoal with a brushing duration of 60 minutes. Measurement of surface roughness (Ra) was carried out using the Mitutoyo SJ-210 Surface Roughness Tester. The research data then analyze statistically. Results: The results of statistical tests showed that there were significant different (p<0.05) between the average surface roughness values of the GIC, RMGIC and Nanoionomer materials after brushing with toothpaste containing charcoal. Conclusion: There are difference in surface roughness values of GIC, RMGIC and Nanoionomer after brushing with charcoal toothpaste.

Item Type: Thesis (Sarjana)
Identification Number: 0520140051
Uncontrolled Keywords: GIC, RMGIC, Nanoionomer, kekasaran permukaan, pasta gigi charcoal,GIC, RMGIC, Nanoionomer, surface roughness, charcoal toothpaste
Subjects: 600 Technology (Applied sciences) > 617 Surgery, regional medicine, dentistry, ophthalmology, otology, audiology > 617.6 Dentistry
Divisions: Fakultas Kedokteran Gigi > Kedokteran Gigi
Depositing User: soegeng sugeng
Date Deposited: 17 Jun 2022 02:51
Last Modified: 17 Jun 2022 02:51
URI: http://repository.ub.ac.id/id/eprint/191284
[thumbnail of DALAM MASA EMBARGO] Text (DALAM MASA EMBARGO)
Juliastri Maria Katili.pdf
Restricted to Registered users only until 31 December 2022.

Download (2MB)

Actions (login required)

View Item View Item