Sujita, - (2019) Difusi Atom Karbon Pada Proses Pack Carburizing Baja Karbon Dengan Media Carburizer Arang Tongkol Jagung Dan Cangkang Kerang Mutiara. Doctor thesis, Universitas Brawijaya.
Abstract
Baja Struktural steel SS400 merupakan merupakan baja karbon rendah yang biasa di pakai untuk membuat alat-alat pertanian, memiliki angka kekerasan rendah.. Baja AISI420 adalah baja karbon tinggi yang di gunakan untuk pembuatan alat-alat potong, karena memiliki angka kekerasan tinggi. Untuk merekayasa angka kekerasannya, sesuai penggunaannya dilakukan dengan proses pack carburizng untuk baja SS400, dan proses pack decarburizng untuk baja AISI420. Pada penelitian ini dilakukan proses perlakuan panas pack carburizing pada spesimen baja SS400 dan proses pack decarburizng untuk baja AISI42, dengan media carburizer alternatif berupa campuran arang tongkol jagung dan serbuk cangkang mutiara. Pack carburizing pada penelitian dilakukan dua variasi suhu (8750C, dan 9000C), tiga variasi waktu (1, 2, dan 3 jam), tiga variasi persentase penambahan serbuk cangkang kerang mutiara (10%, 20% dan 30% SCKM) pada media carburizer, pack decarburizing dilakukan dengan dua variasi suhu (8000C, dan 9000C), variasi waktu dan variasi persentase penambahan SCKM pada media carburizer sama dengan proses Pack carburizing. Tujuannya untuk menggetahui pengaruhnya terhadap difusi karbon yang ditandai dengan perubahan angka kekerasan permukaan, ketebalan lapisan karburasi, kandungan karbon pada permukaan dan perubahan struktur mikro. Hasil dari penelitian bahwa suhu, waktu karburasi dan penambahan SCKM, mempengaruhi difusi karbon pada proses pack carburizing baja SS400 dan pack decarburizing baja AISI420. Hal ini ditandai dengan adanya kenaikan angka kekerasan 413%, ketebalan lapisan karburasi 825µm ((21% dibawah lapisan karburasi teoritis), persentase kandungan karbon pada permukaan 235%, terbentuk struktur martensit yang lebih halus, pada suhu 9000C, waktu karburasi 3 jam dan 30% penambahan SCKM pada media carburizer. Demikian pula pada proses pack decarburizing baja AISI420 pada suhu 9000C, waktu karburasi 3 jam dan 30% penambahan SCKM pada media carburizer menhasilkan pernurunan angka kekerasan 63%, ketebalan lapisan karburasi 47%, persentase kandungan karbon pada permukaan 76 %. Struktur mikro sebagian besar dalam bentuk ferit dan perlit
English Abstract
In this study the heat treatment of pack carburizing was carried out on SS400 steel specimens and the pack decarburizng process for steel AISI42, with an alternative carburizer medium in the form of a mixture of corn cob charcoal and pinctada maxima shell powder (PMSP). The carburizing pack in the study carried out two temperature variations (875 oC and 900 oC), three time variations (1, 2, and 3 hours), three variations in the percentage of pearl oyster shell powder (10%, 20% and 30% PMSP) on the carburizer media , the pack decarburizing pack is done with two temperature variations (800 oC, and 900 oC), time variations and variations in the percentage of PMSP addition on the carburizer media are the same as the carburizing pack process. The aim is to find out the effect on carbon diffusion which is characterized by changes in the number of surface hardness, thickness of the carburizing layer, carbon content on the surface and changes in microstructure. The results of the study that the temperature, carburizing time and the addition of PMSP, affect the diffusion of carbon in the SS400 steel carburizing pack process and the AISI420 steel decarburizing pack. This is indicated by an increase in the number of hardness of 413%, thickness of the carburizing layer 825µm ((21% below the theoretical carburizing layer), percentage of carbon content on the surface of 235%, finer martensitic structure formed, at 9000C, carburizing time of 3 hours and 30 % of the addition of PMSP on the carburizer media Similarly, the process of decarburizing steel AISI420 at 900 oC, carburizing time of 3 hours and 30% addition of PMSP on carburizer media resulted in a decrease in hardness of 63%, carburizing thickness of 47%, percentage of carbon content on surface % The microstructure is mostly in the form of ferrite and pearlite
| Item Type: | Thesis (Doctor) |
|---|---|
| Identification Number: | DIS/372.36/SUJ/d/2019/061904235 |
| Uncontrolled Keywords: | serbuk cangkang kerang mutiara, arang tongkol jagung, proses pack carburizing, proses pack decarburizing, difusi karbon, media carburizer, baja SS400, baja AISI420 |
| Subjects: | 600 Technology (Applied sciences) > 672 Iron, steel other iron alloys |
| Divisions: | S2/S3 > Doktor Teknik Mesin, Fakultas Teknik |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 17 Nov 2021 07:40 |
| Last Modified: | 14 Mar 2022 04:54 |
| URI: | http://repository.ub.ac.id/id/eprint/186717 |
Preview |
Text
SUJITA.pdf Download (3MB) | Preview |
Actions (login required)
 |
View Item |