Anwar, Muchammad Zainul (2019) Studi Aktivasi Katalis Fischer Tropsch Berbasis Besi (Fe) Yang Disintesis Dengan Metode SOL-GEL. Magister thesis, Universitas Brawijaya.
Abstract
Reaksi Fischer Tropsch (FT) adalah reaksi konversi gas sintesis (CO + H2) menjadi campuran hidrokarbon rantai panjang. Katalis FT merupaka salah satu komponen penting dalam reaksi FT. Tujuan penelitian ini adalah mempelelajari aktivasi katalis fischer tropsch (FT) berbasis besi (Fe) yang disintesis dengan metode sol-gel. Perlakuan perbedaan suhu kalsinasi dan perbedaan metode pengaliran gas pada proses aktivasi dilakukan untuk mengetahui pengaruh suhu kalsinasi terhadap fase yang muncul pada katalis. Penelitian ini menggunakan perbandingan komposisi Fe:Cu sebesar 20:1. Suhu kalsinasi dibuat dengan variasi 300, 500, dan 700°C. Aktivasi metode 1 yaitu dengan mengalirkan gas H2 diikuti gas H2+CO2, aktivasi metode 2 yaitu langsung mengalirkan gas H2+CO2. Hasil sintesis menunjukkan katalis sebelum aktivasi yang paling baik adalah katalis dengan suhu kalsinasi 300°C (C-300) dan 500°C (C-500) karena hasil karakterisasi menggunakan XRD menunjukkan munculnya fase besi oksida. Aktivasi pada masing-masing katalis mengakibatkan munculnya fase Fe valensi nol pada C-300 activated dan C-500 activated. Aktivasi pada C-700 tidak mengubah fase yang muncul, hal ini disebabkan karena pada C-700 telah terbentuk fase yang stabil. Perbedaan metode aktivasi dilakukan untuk membandingkan metode aktivasi yang lebih baik. Studi metode aktivasi dilakukan terhadap sampel C-500. Hasil karakterisasi XRD menunjukkan metode aktivasi 1 lebih baik daripada metode 2 yang ditandai dengan munculnya fase Fe3C pada katalis yang diaktivasi dengan metode 1, dan tidak muncul pada katalis yang diaktivasi dengan metode 2. Hasil ini juga didukung dari data karakterisasi EDS.
English Abstract
Fischer Tropsch (FT) reaction is a synthesis gas conversion reaction (CO+H2) into a long chain hydrocarbon mixture. The FT catalyst is one of the important components in the FT reaction. The purpose of this study was to study the activation of iron (Fe) based fischer tropsch (FT) catalysts synthesized by the sol-gel method. The treatment of the difference in calcination temperature and the difference in the activation method was carried out to determine the effect of the calcination temperature on the phase that appeared on the catalyst. This study uses a composition ratio of Fe: Cu of 20: 1. The temperature of calcination is made with variations of 300, 500, and 700°C. Activation of method 1 is by flowing H2 gas followed by H2+CO2 gas, activating method 2 which is direct flowing H2+CO2 gas. The synthesis results showed that the best catalyst before activation was a catalyst with a calcination temperature of 300°C (C-300) and 500°C (C-500) because the results of characterization using XRD showed the appearance of an iron oxide phase. Activation of each catalyst resulted Fe zero valence phase on C-300 activated and C-500 activated. Activation on the C-700 does not change the phase that appears, this is due to the stable phase of the C-700. The difference in the activation method is done to compare better activation methods. The activation method study was carried out on the C-500 sample. The XRD characterization results show that the activation method 1 is better than method 2 which is characterized by the appearance of Fe3C phase on the catalyst activated by method 1, and does not appear on catalysts activated by method 2. This result is also supported from EDS characterization data.
Other obstract
-
| Item Type: | Thesis (Magister) |
|---|---|
| Identification Number: | TES/662.662 3/ANW/s/2019/041904287 |
| Uncontrolled Keywords: | FISHER - TROPSCH PROCESS, CATALYSIS |
| Subjects: | 600 Technology (Applied sciences) > 662 Explosives of explosives, fuels, related products > 662.6 Fuels > 662.66 Synthetic fuels > 662.662 Synthetic Petroleum > 662.662 3 Production of synthetic petroleum through hydrogenation and liquefaction of coal |
| Divisions: | S2/S3 > Magister Kimia, Fakultas MIPA |
| Depositing User: | Endang Susworini |
| Date Deposited: | 12 Mar 2020 03:54 |
| Last Modified: | 12 Mar 2020 03:54 |
| URI: | http://repository.ub.ac.id/id/eprint/180323 |
Actions (login required)
 |
View Item |