Pengaruh Pembersih Gigi Tiruan Ekstrak Buah Nanas 30% (Ananas Comosus L.Merr) Terhadap Kekuatan Transversa Resin Akrilik Polimerisasi Panas

Safitri, Aulia Rachma Deny (2019) Pengaruh Pembersih Gigi Tiruan Ekstrak Buah Nanas 30% (Ananas Comosus L.Merr) Terhadap Kekuatan Transversa Resin Akrilik Polimerisasi Panas. Sarjana thesis, Universitas Brawijaya.

Abstract

Resin akrilik polimerisasi panas merupakan material yang sering digunakan dalam pembuatan basis gigi tiruan. Pembersihan resin akrilik pada gigi tiruan secara rutin perlu dilakukan dengan baik, karena dapat mencegah pembentukan mikroorganisme. Metode dengan pembersihan kimia memiliki kekurangan seperti bau tidak sedap dan dapat meningkatkan kekasaran resin akrilik. Sehingga saat ini banyak dikembangkan pembersih gigi tiruan dari bahan alami salah satunya ekstrak buah nanas. Pada penelitian Ika Astrina (2012) pembersih gigi tiruan ekstrak buah nanas 30% terbukti dapat menurunkan jumlah koloni Candida albicans, sehingga dapat digunakan sebagai bahan alternatif pembersih gigi tiruan. Penelitian ini bertujuan untuk mengetahui pengaruh pembersih gigi tiruan ekstrak buah nanas 30% terhadap kekuatan transversa. Jenis penelitian ini adalah eksperimental laboratoris. Sebanyak 24 sampel resin akrilik polimerisasi panas dengan dimensi 65 mm x 10 mm x 2,5 mm. Sampel dibagi menjadi 4 kelompok, direndam dengan ekstrak buah nanas 30% dan akuades dengan waktu perendaman 11 hari dan 18 hari. Setelah perendaman lempeng akrilik dilakukan uji trasversa dengan alat Universal testing Machine. Hasil uji kekuatan transversa dianalisis menggunakan uji one way ANOVA. Dari hasil uji kekuatan transversa terdapat perbedaan yang bermakna (α ˂0.05) yaitu terjadi penurunan kekuatan transversa resin akrilik polimerisasi panas pada kelompok perlakuan setelah perendaman dalam pembersih gigi tiruan ekstrak buah nanas 30% selama 11 hari dan 18 hari. Kesimpulan dari penelitian ini adalah perendaman lempeng resin akrilik polimerisasi panas dalam ekstrak buah nanas 30% sebagai pembersih gigi tiruan berpengaruh menurunkan kekuatan transversa.

English Abstract

Heat polymerized acrylic resin is a material that is often used in making denture bases. Cleaning acrylic resin on denture routinely needs to be done well, because it can prevent the formation of microorganisms. The method with chemical cleaning has disadvantages such as bad odor and can increase the roughness of acrylic resin. So that currently many denture cleansers are developed from natural ingredients, one of which is pineapple fruit extract. In the study of Ika Astrina (2012) denture cleanser of 30% pineapple fruit extract was proven to reduce the number of colonies of Candida albicans, so that it can be used as an alternative material for denture cleansers. This study aims to determine the effect of 30% pineapple fruit extract extract teeth cleanser on transverse strength. This type of research is an experimental laboratory. A total of 24 heat polymerization acrylic resin samples with dimensions of 65 mm x 10 mm x 2.5 mm. The samples were divided into 4 groups, soaked with pineapple fruit extract 30% and akuades with immersion time 11 days and 18 days. After immersion of the acrylic plate trasversa test was performed with a Universal testing Machine. The transverse strength test results were analyzed using one way ANOVA test. From the results of the transverse strength test there were significant differences x (α ˂0.05), namely a decrease in the transverse strength of heat polymerization acrylic resin in the treatment group after immersion in pineapple extract 30% for 11 days and 18 days. The conclusion of this study is the immersion of hot polymerization acrylic resin plates in 30% pineapple fruit extract as a denture cleaner has an effect on reducing transverse strength.

Item Type: Thesis (Sarjana)
Identification Number: SKR/FKG/2019/105/052001859
Uncontrolled Keywords: pembersih gigi tiruan, ekstrak buah nanas 30% (Ananas Comosus L.Merr), resin akrilik polimerisasi panas, kekuatan transversa-denture cleanser, 30% pineapple fruit extract (Ananas Comosus L.Merr), heat polymerization acrylic resin, transverse strength.
Subjects: 600 Technology (Applied sciences) > 617 Surgery, regional medicine, dentistry, ophthalmology, otology, audiology > 617.6 Dentistry > 617.66 Extraction / Teeth--Extraction
Divisions: Fakultas Kedokteran Gigi > Kedokteran Gigi
Depositing User: soegeng sugeng
Date Deposited: 10 Aug 2020 07:56
Last Modified: 23 Oct 2021 03:03
URI: http://repository.ub.ac.id/id/eprint/179161
[thumbnail of Aulia Rachma Deny Safitri.pdf]
Preview
Text
Aulia Rachma Deny Safitri.pdf

Download (4MB) | Preview
[thumbnail of makalah_Aulia Rachma_155070407111028.pdf]
Preview
Text
makalah_Aulia Rachma_155070407111028.pdf

Download (3MB) | Preview

Actions (login required)

View Item View Item