Angga, Stevin Carolius (2018) Sintesis Polimer Metakrilat sebagai Fasa Diam Kolom HPLC serta Modifikasinya Dalam Pemisahan Senyawa Khiral. Magister thesis, Universitas Brawijaya.
Abstract
Kolom monolit berbasis polimer metakrilat dapat dibuat dengan cukup mudah secara in situ kopolimerisasi, selain itu dapat pula dimodifikasi lebih lanjut. Sementara itu, senyawa etilendiamin-β-siklodekstrin (EDA-β-CD) mampu dimanfaatkan dalam pemisahan senyawa khiral. Dalam penelitian ini teknologi monolit polimer organik berbasis metakrilat dikembangkan sebagai fasa diam kolom kemudian dimodifikasi lebih lanjut dengan EDA-β-CD sebagai fasa diam kolom khiral. Kolom monolit dari polimer organik disintesis secara in situ kopolimerisasi di dalam polietereterketon (PEEK) tubing (1.0 mm i.d. x 10 mm) dari glisidil metakrilat (GMA) dan trimetilolpropana trimetakrilat (TMPTMA) dengan keberadaan porogen 1-propanol, 1,4-butanadiol, dan air disertai dengan inisiator radikal α,α-azobutironitril (AIBN). Monolit poli-(GMA-co-TMPTMA) dibuat dalam enam variasi komposisi total monomer (%T) dan crosslinker (%C) untuk memperoleh kolom dengan tekanan balik yang rendah. Setelah komposisi yang terbaik diperoleh, kolom diaplikasikan untuk memisahkan toluena dan amil benzena. Sementara itu, kolom dengan komposisi terbaik dibuat kembali dan dimodifikasi dengan EDA-β-CD untuk memperoleh kolom khiral poli-(GMAEDA- β-CD-co-TMPTMA) lalu diaplikasikan untuk memisahkan (±)-sitronelal. Dari hasil karakterisasi enam variasi kolom monolit poli-(GMA-co- TMPTMA) dengan %T 30 dan %C 20 merupakan komposisi yang terbaik. Kolom tersebut mampu memisahkan toluena dan amil benzena pada waktu retensi 84 dan 132 menit. Sementara itu, kolom poli-(GMA-EDA-β-CD-co-TMPTMA) mampu memisahkan (±)-sitronelal pada waktu retensi 44 dan 45 menit.
English Abstract
The methacrylate-based monolithic column could be produced by simple preparation of in situ copolymerization, moreover it may also modified for futher stage. Meanwhile, ethylenediamine-β-cyclodextrin (EDA-β-CD) may be utilized in the separation of chiral compounds. In this study, methacrylate-based monolithic polymer technology was developed as stationary phase column and used for further modification of EDA-β-CD as the chiral stationary phase column. The monolithic column of organic polymer was synthesized by in situ copolymerization in polyethereterketone (PEEK) tubing (1.0 mm id x 10 mm) from glycidyl methacrylate (GMA) and trimethylolpropane trimethacrylate (TMPTMA) in the presence of porogen 1-propanol, 1,4-butanadiol, and water in addition of α, α-azobutironitrile (AIBN) as radical initiator. Poly-(GMA-co- TMPTMA) were made in six composition variation of the total monomer (% T) and crosslinker (% C) to obtain column with low backpressure. Afterwards the column with best lowest backpressure is applied to separates toluene and amyl benzene. Meanwhile, it was remade and modified with EDA-β-CD to produce poly-(GMA-EDA-β-CD-co-TMPTMA) chiral column and then applied to separates (±)-citronellal. The results of the characterization of six variations of poly monolithic columns (GMA-co-TMPTMA) with %T 30 and %C 20 was found to be the best composition. The column was able to separate toluene and amyl benzene at a retention time of 84 and 132 min. Meanwhile, the poly (GMA-EDA-β-CD-co- TMPTMA) column was able to separate (±)-citronellal at 44 and 45 min.
Other obstract
-
| Item Type: | Thesis (Magister) |
|---|---|
| Identification Number: | TES/546/ANG/s/2018/041901348 |
| Uncontrolled Keywords: | INORGANIC CHEMISTRY, CHEMISTRY, INORGANIC |
| Subjects: | 500 Natural sciences and mathematics > 546 Inorganic chemistry |
| Divisions: | S2/S3 > Magister Kimia, Fakultas MIPA |
| Depositing User: | Endang Susworini |
| Date Deposited: | 08 Jan 2020 02:51 |
| Last Modified: | 08 Jan 2020 02:51 |
| URI: | http://repository.ub.ac.id/id/eprint/177627 |
Actions (login required)
 |
View Item |