Hendrayana, Peter Dewa (2019) Pengaruh Variasi Waktu Tembak Sandblasting dan Kadar Larutan Electropolishing Terhadap Laju Korosi Material Stainless Steel AISI 316L. Sarjana thesis, Universitas Brawijaya.
Abstract
Penelitian ini ditujukan untuk mengetahui pengaruh dari waktu tembak sandblasting dan kadar larutan electropolishing terhadap laju korosi pada material stainless steel AISI 316L. Electropolishing adalah teknik finishing/polishing permukaan secara elektrokimia dan sandblasting adalah metode perlakuan permukaan untuk meningkatkan sifat mekanik material. Alat yang digunakan adalah mesin sandblasting dengan tekanan kerja 5 bar dengan durasi 5 menit 10 menit dan 15 menit. Pasir yang digunakan adalah pasir silika dengan ukuran 100-400μm. Alat yang digunakan pada proses electropolishing adalah DC power supply dengan output maximum 30V. Material anoda dan katoda adalah stainless steel AISI 316L, sementara kadar larutan electropolishing yang dipergunakan adalah 15%wt H2SO4 dengan 65%wt H3PO4 dan 35%wt H2SO4 dengan 45%wt H3PO4 sehingga menghasilkan enam variasi pengujian. Pertama kali, spesimen diperlakukan dengan perlakuan sandblasting, kemudian dilanjukan dengan perlakuan electropolishing sesuai dengan parameter yang telah ditetapkan untuk keduanya. Kemudian setelah perlakuan diatas selesai dilanjutkan dengan pengujian dan diperoleh data berupa laju korosi dan data tambahan berupa kekasaran permukaan. Hasil pengujian menunjukkan bahwa waktu sandblasting 15 menit dengan kombinasi larutan 15%wt H2SO4 dengan 65%wt H3PO4 menghasilkan laju korosi terbesar yaitu 0.008 mmpy. Sedangkan waktu sandblasting 5 menit dengan kombinasi larutan 35%wt H2SO4 dengan 45%wt H3PO4 menghasilkan laju korosi paling rendah yaitu sebesar 0.0022 mmpy. Diperkuat juga oleh kekasaran permukaan yang senada dengan laju korosinya yang tertinggi sebesar 2.304μm dan terendah sebesar 0.784μm.
English Abstract
This research is aimed to find out the effect from sandblasting duration and electropolishing concentration on the corrosion rate of stainless steel AISI 316L material. Electropolishing is a surface finishing/polishing method in electrochemically and sandblasting is surface treatment method to enhance mechanical properties of the material. The equipment used was sandblasting machine with a working pressure of 5 bars with duration of 5 minutes 10 minutes and 15 minutes. The abrasive material used was silica sand with grain size of 100-400μm. The equipment used in the electropolishing process is a DC power supply with a maximum output of 30Volt. The anode and cathode material were stainless steel AISI 316L, While the concentration of electropolishing solution is 15%wt H2SO4 with 65%wt H3PO4 and 35%wt H2SO4 with 45%wt H3PO4 with the result that made six variation of test. First, the specimens is treated with sandblasting, the continued with electropolishing treatment according to the parameters sets for both treatments. Then, after those treatments is completed, followed by testing and data obtained in form of corrosion rate and additional data in form of surface roughness. Test result shows that sandblast duration of 15 minutes with combination of 15%wt H2SO4 with 65%wt H3PO4 electropolish solution gives largest corrosion rate with 0.008 mmpy. While sandblast duration of 5 minutes and combination of 35%wt H2SO4 with 45%wt H3PO4 gives smallest corrosion rate in amount of 0.0022 mmpy. Also strengthened by data from surface roughness with highest value of 2.304μm for highest corrosion rate and lowest value of 0.784μm for lowest corrosion rate.
Other obstract
-
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FT/2019/509/051905105 |
| Uncontrolled Keywords: | Stainless steel AISI 316L, sandblasting, electropolishing, kekasaran, laju korosi, Stainless steel AISI 316L, sandblasting, electropolishing, surface roughness, corrosion rate |
| Subjects: | 600 Technology (Applied sciences) > 620 Engineering and allied operations > 620.1 Engineering mechanics and materials > 620.11 Engineering materials > 620.112 Properties of materials and nondestructive testing |
| Divisions: | Fakultas Teknik > Teknik Mesin |
| Depositing User: | Budi Wahyono Wahyono |
| Date Deposited: | 01 Nov 2020 08:31 |
| Last Modified: | 01 Nov 2020 08:31 |
| URI: | http://repository.ub.ac.id/id/eprint/173490 |
Actions (login required)
 |
View Item |