Pengaruh Variasi Suhu Karbonisasi Dan Jenis Activator Agent Terhadap Karakteristik Karbon Aktif Dari Limbah Kayu Sengon (Paraserianthes Falcataria (L.) Nielsen

Sajidah, Nisrina (2018) Pengaruh Variasi Suhu Karbonisasi Dan Jenis Activator Agent Terhadap Karakteristik Karbon Aktif Dari Limbah Kayu Sengon (Paraserianthes Falcataria (L.) Nielsen. Sarjana thesis, Universitas Brawijaya.

Abstract

Limbah kayu sengon mengandung lignin sebesar 26,50%. Kandungan lignin inilah yang bisa membuat limbah kayu sengon diolah menjadi karbon aktif. Karbon aktif merupakan padatan berpori yang mengandung 85 – 95% karbon. Karbon aktif dihasilkan dari bahan yang mengandung karbon dengan pemanasan suhu tinggi. Proses pembuatan karbon aktif sendiri terdiri dari dehidrasi, karbonisasi, dan aktivasi. Aktivasi dapat dilakukan secara kimia. Aktivasi kimia dapat dilakukan dengan menggunakan bahan kimia tertentu untuk dicampur dengan karbon. Tujuan dari penelitian ini adalah menganalisis pengaruh suhu karbonisasi terhadap kualitas dan karakteristik karbon aktif dari kayu sengon, menganalisis pengaruh aktivator terhadap kualitas dan karakteristik karbon aktif dari kayu sengon dan karakterisasi karbon aktif dari kayu sengon dengan perbedaan suhu aktivasi dan jenis aktivator. Rancangan percobaan yang digunakan adalah rancangan acak kelompok yang disusun secara faktorial dengan 2 faktor, faktor I adalah suhu karbonisasi (suhu 400, 500 dan 600 °C dan faktor II merupakan jenis activator agent (aktivator ZnCl2, CaCl2, dan CH3COOH). Masing-masing perlakuan diulang sebanyak 3 kali. Pengujian yang dilakukan adalah pengujian kadar air, pengujian daya serap iodin dan perhitungan luas permukaan. Hasil perlakuan terbaik akan diuji morfologinya oleh SEM-EDX. Pada penelitian ini diperoleh hasil suhu karbonisasi dan jenis activator agent berpengaruh nyata terhadap karakter karbon aktif yang dihasilkan. Hasil terbaik ditunjukkan oleh karbon dengan suhu karbonisasi 600 °C dengan activator agent CaCl2 yaitu dengan nilai kadar air sebesar 1,46%, daya serap iodin sebesar 1089,5598 mg/g dan luas permukaan sebesar 1201,5688 m2/g.

English Abstract

The sengon wood waste contains lignin of 26.50%. Lignin content is what can make the waste sengon wood processed into activated carbon. Activated carbon is a porous solid containing 85 - 95% carbon. Activated carbon is produced from carbonaceous materials with high temperature heating. The process of making activated carbon are dehydration, carbonization, and activation. Activation can be done chemically. Chemical activation can be done by using certain chemicals to be mixed with carbon. The purpose of this study was to analyze the effect of carbonization temperature on the quality and characteristics of activated carbon from sengon wood, to analyze the effect of activator on the quality and characteristics of activated carbon from sengon wood and the characterization of activated carbon from sengon wood with different activation temperature and activator type. The experimental design used was a factorial randomized block design with 2 factors, factor I was carbonization temperature (temperature 400, 500 and 600 ° C and factor II was activator agent type (activator ZnCl2, CaCl2, and CH3COOH) Each treatment was repeated 3 times. The test is water test, iodine absorption test and surface area calculation. The best treatment result will be tested its morphology by SEM-EDX. In this research, the result of carbonization temperature and activator agent type have real effect to character of the activated carbon The best result is shown by carbon with carbonization temperature of 600 ° C with CaCl2 activator agent with 1.46% moisture content, iodine absorption of 1089,5598 mg / g and surface area of 1201,5688 m2 / g.

Item Type: Thesis (Sarjana)
Identification Number: SKR/FTP/2018/268/051807904
Uncontrolled Keywords: activator agent, karbon aktif, kayu sengon, suhu karbonisasi / activator agent, activated carbon, carbonization temperature, sengon wood
Subjects: 500 Natural sciences and mathematics > 549 Mineralogy > 549.7 Other minerals
Divisions: Fakultas Teknologi Pertanian > Keteknikan Pertanian
Depositing User: Endang Susworini
Date Deposited: 04 Nov 2019 02:19
Last Modified: 01 Jul 2022 03:00
URI: http://repository.ub.ac.id/id/eprint/165967
[thumbnail of Nisrina Sajidah.pdf] Text
Nisrina Sajidah.pdf

Download (5MB)

Actions (login required)

View Item View Item