Amanah, Ana (2017) Sintesis Dan Karakterisasi Membran Mixed Matrix Berbasis Selulosa Asetat-Nanokarbon Aktif Dari Tandan Kosong Kelapa Sawit Sebagai Adsorben Gas Emisi Sepeda Motor. Sarjana thesis, Universitas Brawijaya.
Abstract
Indonesia merupakan negara dengan populasi motor terbanyak ketiga di Asia. Jumlah sepeda motor di Indonesia meningkat sepanjang tahun 2003-2013. Peningkatan ini berbanding lurus dengan peningkatan emisi polutan sepeda motor, seperti CO, CO2, dan HC, sehingga diperlukan upaya adsorpsi dalam rangka mengurangi polutan pencemar udara. Tandan Kosong Kelapa Sawit (TKKS) merupakan salah satu limbah padat terbesar dalam industri pengolahan sawit di Indonesia. Kandungan lignoselulosa dalam TKKS cukup tinggi, sehingga TKKS berpotensi menjadi bahan baku pembuatan selulosa asetat (CA) dan nanokarbon aktif (NAC) guna sintesis Membran Mixed Matrix (MMM) sebagai adsorben. Tujuan dari penelitian ini adalah untuk mengetahui proses sintesis MMM serta komposisi larutan cetak MMM terbaik dalam mengadsorpsi CO, CO2, dan HC. Penelitian ini menggunakan metode analisis deskriptif. Lima tahapan proses utama pada penelitian ini adalah isolasi selulosa dari TKKS, sintesis CA, pembuatan NAC, sintesis MMM, dan karakterisasi MMM. Hasil uji performansi MMM terbaik untuk tingkat adsorpsi CO dan CO2 diberikan oleh MMM dengan rasio CA:NAC = 4:3, sedangkan tingkat adsorpsi HC tertinggi dilakukan oleh MMM dengan rasio CA:NAC = 4:5. Kendati demikian komposisi larutan MMM terbaik adalah MMM dengan rasio CA:NAC = 4:3.
English Abstract
Indonesia is a country with third highest motorcycle population in Asia. The number of motorcycle population in Indonesia increased since 2003 to 2013. This increase is directly proportional to the increase of motorcycle pollutant emissions, such as CO, CO2 and HC, so the adsorption becomes necessary in order to reduce air pollution. Oil Palm Empty Fruit Bunch (EFB) is one of the largest solid waste in the oil processing industry in Indonesia. The content of lignocellulose in EFB is high, so EFB potentially to be raw material in the manufacture of cellulose acetate (CA) and nanoactivated carbon (NAC) for the synthesis of Mixed Matrix Membrane (MMM). The purpose of this study was to determine the synthesis of MMM and its best casting solution in CO, CO2 and HC adsorption. This study used descriptive analysis method. Five main processes are extraction of cellulose from EFB, CA synthesis, manufacture of NAC, MMM synthesis, and characterization of MMM. Performance test results showed that the adsorption of CO and CO2 levels given by MMM with ratio of CA:NAC = 4:3, whereas the highest level of HC adsorption done by MMM with ratio of CA:NAC = 4:5. The best casting solution for synthesis MMM was membrane with ratio of CA:NAC = 4:3.
| Item Type: | Thesis (Sarjana) |
|---|---|
| Identification Number: | SKR/FTP/2017/112/051702570 |
| Subjects: | 300 Social sciences > 338 Production > 338.1 Agriculture |
| Divisions: | Fakultas Teknologi Pertanian > Keteknikan Pertanian |
| Depositing User: | Kustati |
| Date Deposited: | 06 Mar 2017 15:16 |
| Last Modified: | 22 Oct 2021 02:25 |
| URI: | http://repository.ub.ac.id/id/eprint/151338 |
Preview |
Text
Ana_Amanah_135100900111024_TA_Teknik_Lingkungan.pdf Download (4MB) | Preview |
Actions (login required)
 |
View Item |