Pengaruh Penggunaan Mineral Lokal Zeolit Alam Terhadap Karakteristik Self-Compacting Concrete (SCC).

Poerwadi, Mahmud Rekarifin (2014) Pengaruh Penggunaan Mineral Lokal Zeolit Alam Terhadap Karakteristik Self-Compacting Concrete (SCC). Sarjana thesis, Universitas Brawijaya.

Abstract

Self-Compacting Concrete (SCC) adalah sebuah inovasi dalam teknologi pembuatan beton yang tidak memerlukan proses pemadatan untuk menempati bekistingnya dan memadat sendiri. Pada penelitian ini pembuatan SCC digunakan untuk memanfaatkan potensi material lokal zeolit alam. Penelitian dilakukan melalui pembuatan 3 benda uji pada variasi SCC tanpa zeolit alam dan SCC yang ditambahkan kadar zeolit alam 5%, 10%, dan 15% dari berat semen yang digunakan dalam campuran dengan penggunaan additon slumpflow sebesar 1,5% dari berat semen dan FAS yang digunakan sebesar 0,49. Pengujian yang dilakukan adalah pengujian setting time, filling ability dan kuat tekan beton. Selain itu juga dilakukan perbandingan analisis biaya antara SCC tanpa zeolit alam dengan SCC yang menggunakan zeolit alam Hasil penelitian yang didapatkan adalah kadar zeolit alam yang diberikan berpengaruh terhadap setting time SCC, semakin tinggi kadar zeolit alam yang diberikan sebagai pengganti sebagian semen maka semakin lama waktu yang dibutuhkan untuk mencapai initial dan final setting time. Filling ability beton meningkat sesuai kenaikkan jumlah zeolit alam yang diberikan Kuat tekan optimum yang didapat pada umur 28 hari adalah 28,06 MPa dengan kadar zeolit alam yang diberikan sebesar 10%. Jika ditinjau dari hasil penambahan variasi zeolit alam dengan kuat tekan beton yang dihasilkan, nilai optimum yang didapat dari persamaan regresi y = -0,0605x2-1,3865 adalah sebesar 11,45%. Penggunaan zeolit alam sebagai pengganti sebagian semen dapat mengurangi biaya pembuatan SCC. Namun pembuatan SCC dengan menggunakan zeolit alam tidak memiliki perbedaan yang signifikan jika dilihat dari sisi ekonomis.

English Abstract

Self-Compacting Concrete (SCC) is a technological innovation in the manufacture of concrete that does not require compaction process to occupy formwork and solidified himself. In this research the manufacture of SCC used to harness the potential of local natural zeolite material. The research was conducted through the manufacture of test specimens in 3 variations SCC without natural zeolite and natural zeolite were added levels of 5%, 10%, and 15% of the weight of the cement used in the mix with the use slump flow additon of 1.5% of the weight of cement and FAS used at 0.49. Tests were performed is testing setting time, filling ability and strength of concrete. It also conducted a cost analysis comparison between SCC without natural zeolite with SCC using natural zeolite Research results obtained are given natural zeolite levels affect the setting time of SCC, the higher levels of natural zeolite as a partial replacement of cement given the longer time required to reach the initial and final setting time. Filling ability of concrete increased accordingly increase the amount of natural zeolites are given optimum compressive strength obtained at 28 days was 28.06 MPa with high levels of natural zeolite were given by 10%. If viewed from the increased variety of natural zeolite with a compressive strength of concrete produced, the optimum value obtained from the regression equation y = -0,0605x2-1,3865 amounted to 11.45%. The use of natural zeolite as a partial replacement for cement can reduce the cost of making SCC. However, SCC manufacture using natural zeolite does not have significant difference when viewed from the economical.

Item Type: Thesis (Sarjana)
Identification Number: SKR/FT/2014/381/051404864
Subjects: 600 Technology (Applied sciences) > 670 Manufacturing
Divisions: Fakultas Teknik > Teknik Industri
Depositing User: Hasbi
Date Deposited: 15 Sep 2014 09:22
Last Modified: 15 Nov 2021 05:54
URI: http://repository.ub.ac.id/id/eprint/142672
[thumbnail of 4_Ringkasan.pdf]
Preview
Text
4_Ringkasan.pdf

Download (1MB) | Preview
[thumbnail of 5_BAB_I.pdf]
Preview
Text
5_BAB_I.pdf

Download (1MB) | Preview
[thumbnail of 6_BAB_II.pdf]
Preview
Text
6_BAB_II.pdf

Download (2MB) | Preview
[thumbnail of 7_BAB_III.pdf]
Preview
Text
7_BAB_III.pdf

Download (2MB) | Preview
[thumbnail of 8_BAB_IV.pdf]
Preview
Text
8_BAB_IV.pdf

Download (2MB) | Preview
[thumbnail of 9_BAB_V.pdf]
Preview
Text
9_BAB_V.pdf

Download (1MB) | Preview
[thumbnail of 11_Lampiran.pdf]
Preview
Text
11_Lampiran.pdf

Download (3MB) | Preview
[thumbnail of 10_Daftar_Pustaka.pdf]
Preview
Text
10_Daftar_Pustaka.pdf

Download (1MB) | Preview
[thumbnail of 1_Judul.pdf]
Preview
Text
1_Judul.pdf

Download (1MB) | Preview
[thumbnail of 2_Kata_Pengantar.pdf]
Preview
Text
2_Kata_Pengantar.pdf

Download (1MB) | Preview
[thumbnail of 3_Daftar_Isi.pdf]
Preview
Text
3_Daftar_Isi.pdf

Download (1MB) | Preview

Actions (login required)

View Item View Item