Safitri, Ananda Ria (2020) Pengaruh Tegangan RF dan Jenis Gas pada Treatment Plasma Terhadap Wettability dan Sifat Mekanik Serat Sabut Kelapa (cocos nucifera). Magister thesis, Universitas Brawijaya.

Indonesian Abstract

Komposit berbahan serat alam semakin banyak dikembangkan karena mudah didapat dan ramah lingkungan. Penggunaan serat alam sebagai penguat komposit memiliki kelemahan pada ikatan interfacial antara serat dan matrik, dimana karakteristiknya melibatkan kemampuan basah serat atau wettability. Dalam penelitian ini dilakukan treatment plasma pada serat dengan pemberian dua jenis gas yang berbeda yaitu argon dan oksigen selain itu diberikan variasi tegangan RF 80, 100, 120, dan 140 volt dan Jenis Gas. Penelitian ini bertujuan menganalisa pengaruh tegangan RF dan jenis gas terhadap wettability dan sifat mekanik serat dan komposit. Hasil penelitian menunjukkan treatment plasma meningkatkan wettability serat dengan menurunnya nilai sudut kontak serat, selain itu juga meningkatkan sifat mekanik serat maupun komposit. Pemberian tegangan RF 80 volt pada treatment plasma argon menghasilkan nilai sudut kontak paling rendah yaitu 65,3 ± 2,7o dan nilai kuat tarik tertinggi yaitu 99,2 ± 2,4 Mpa untuk serat tunggal dan 21,7 ± 0,8 MPa untuk komposit. Sedangkan pada gas oksigen, nilai sudut kontak paling rendah adalah 67,3 ± 1,6o pada pemberian tegangan RF 140 volt dan nilai kuat tarik tertinggi yaitu 97,9 ± 3,1 MPa untuk serat tunggal dan 20,2 ± 0,3 MPa untuk komposit.

English Abstract

Natural fibers composite are increasinglybeing develop because of they are easy to obtain and environmentally friendly. The use of natural fibers as reinforcement for composite has a weakness in the interfacial bond between the fiber and the matrix, where the characteristic involve the fiber’s wettability. In this research, plasma treatment was carried out on the fiber by giving argon and oxygen as variation of gas, and also using RF Voltage at variation 80, 100, 120, and 140 volt. The purpose of this research to know the influence of RF voltage and type of gas on the wettability and mechanical properties of fiber and composite. The result showed that plasma treatment increased fiber wettability by decreasing contact angle and also increasing the mechanical properties of the fiber and composite. The giving of 80 volt RF voltage in the argon plasma treatment was produces the lowest contact angle value is 65,3 ± 2,7o and maximum tensile strength value is 99,2 ± 2,4 Mpa for single fiber and 21,7 ± 0,8 MPa for composite. Whereas in oxygen plasma treatment, the lowest contact angle value is 67,3 ± 1,6o at 140 volt RF voltage and the maximum tensile strength value is 97,9 ± 3,1 MPa for single fiber and 20,2 ± 0,3 MPa for compsoite.

Other Language Abstract

-

Item Type: Thesis (Magister)
Identification Number: 0420090001
Uncontrolled Keywords: Serat sabut kelapa, Treatment plasma, wettability, sifat mekanik.
Subjects: 500 Natural sciences and mathematics > 534 Sound and related vibrations > 534.3 Characteristics of sound
Divisions: Fakultas Matematika dan Ilmu Pengetahuan Alam > Fisika
Depositing User: ismanto
URI: http://repository.ub.ac.id/id/eprint/183660