Imansari, Mila Baarik and Mahardana, Nadia Sjavira (2018) Pengaruh Rasio H2O:Natrium Silikat dan Konsentrasi Katalis NH4OH pada Membran Komposit Silika Hidrofobik dalam Pemisahan CPO-Air. Sarjana thesis, Universitas Brawijaya.

Indonesian Abstract

Membran komposit hidrofobik merupakan membran modifikasi dimana partikel silika hidrofobik didepositkan ke dalam media berupa kain katun. Membran tersebut digunakan dalam pemisahan campuran minyak-air skala laboratorium. Partikel silika hidrofobik dalam penelitian ini difabrikasi dengan metode sol-gel menggunakan prekursor larutan natrium silikat (waterglass) dan agen sililasi berupa TEOS (tetraethoxysilane). Variabel yang ditinjau meliputi rasio H2O:natrium silikat pada 15:1; 16:1; 17:1; 18:1; dan 19:1; dan juga konsentrasi katalis NH4OH 0,1 M, 0,2 M, 0,3 M, 0,4 M, dan 0,5 M. Dengan metode sol-gel, partikel SiO2 akan didepositkan ke dalam membran untuk menciptakan sifat hidrofobisitas yang dihitung berdasarkan nilai sudut kontak butiran air di atas membran. Pemisahan minyak-air dilakukan berdasarkan perbedaan kepolaran dimana membran ini dengan sifat oleofiliknya akan menyerap minyak sehingga minyak dapat melewati membran. Sementara membran juga akan menghalangi air akibat sifat hidrofobiknya. Rasio H2O:natrium silikat pada 18:1 menghasilkan sudut kontak tertinggi sebesar 143.900°. Kemudian rasio 18:1 digunakan untuk variasi katalis NH4OH, dan menghasilkan nilai sudut kontak tertinggi sebesar 157,259° pada konsentrasi 0,4 M. Uji kestabilan hidrofobisitas membran dilakukan selama 5 hari dan didapatkan membran dapat mempertahankan hidrofobisitasnya tanpa ada perubahan signifikan pada sudut kontaknya. Pada proses pemisahan minyak-air, selektivitas membran komposit hidrofobik berdasarkan nilai koefisien rejeksinya (R) tidak menunjukkan perbedaan yang signifikan pada keseluruhan variasi % minyak, yaitu sekitar 0,996-0,999. Hal ini menunjukkan membran komposit dapat memisahkan capuran minyak-air.

English Abstract

The hydrophobic composite membrane is a modified membrane in which silica particles are deposited on cotton fabric medium. The hydrophobic silica particles in this study are fabricated by sol-gel method using sodium silicate (waterglass) solution and a TEOS (tetraethoxysilane) as sililation agent. The variables that examined in this study are the ratio of H2O to sodium silicate of 15: 1; 16: 1; 17: 1; 18: 1; and 19: 1; and NH4OH catalyst concentration of 0.1 M, 0.2 M, 0.3 M, 0.4 M, and 0.5 M. Silica (SiO2) particles are deposited on the membrane to create hydrophobicity which is measured based on the value of contact angle of the water droplet on the membrane surface. Oil-water separation process is based on polar differences in which the membrane with its oleophilic properties absorbs the oil then passes it. While the membrane will block the water due to its hydrophobic nature. The H2O: sodium silicate ratio on 18:1 produces the highest contact angle about 143.900°. By using 18:1 on NH4OH concentration variation, 0.4 M produces the highest contact angle about 157.259°. The hydrophbicity resistance was conducted for 5 days and it was obtained that it could maintain its hydrophobicity without any significant difference. In water-oil separation process, the selectivity of the hydrophobic composite membrane indicated that there is no significant difference in the rejection coefficient (R) in all variation of water-oil percentage ie, 0,996-0,999 which implies that membrane could separate oil-water mixture succesfully.

Other Language Abstract

UNSPECIFIED

Item Type: Thesis (Sarjana)
Identification Number: SKR/FT/2018/358/051804722
Uncontrolled Keywords: hidrofobik, membran, silika, sol-gel
Subjects: 600 Technology (Applied sciences) > 660 Chemical engineering and related technologies
Divisions: Fakultas Teknik > Teknik Kimia
Depositing User: Budi Wahyono
URI: http://repository.ub.ac.id/id/eprint/11803
Text
BAGIAN DEPAN.pdf
Restricted to Repository staff only

Download
Text
BAB I.pdf
Restricted to Repository staff only

Download
Text
BAB II.pdf
Restricted to Repository staff only

Download
Text
BAB III.pdf
Restricted to Repository staff only

Download
Text
BAB IV.pdf
Restricted to Repository staff only

Download
Text
BAB V.pdf
Restricted to Repository staff only

Download
Text
DAFTAR PUSTAKA.pdf
Restricted to Repository staff only

Download

Actions (login required)

View Item View Item